Abstract:
The kinetic parameters of 1%, 2%, 3% and 4% La-doped ZnB2O4 phosphors (i.e. ZnB2O4:0.01La, ZnB2O4:0.02La, ZnB2O4:0.03La and ZnB2O4:0.04La) synthesized by nitric acid method have been calculated. Thermoluminescence (TL) glow curves of ZnB2O4:La phosphors after beta-irradiation showed a very well defined main peak having the maximum temperature at around 200 degrees C and a shoulder peak at around 315 degrees C with a constant heating rate of 5 degrees C/s. The kinetic parameters of ZnB2O4:La phosphors TL glow peaks (i.e. order of kinetics (b), activation energies (E-a) and frequency factors (s)) have been determined and evaluated by Computerized Glow Curve Deconvolution (CGCD), and Peak Shape (PS) methods using the glow curve data. From the results, it can conclude that the values of E-a obtained with these methods for ZnB2O4:La phosphors are consistent with each other, but the s values differ considerably.